Aluminum Oxide Ceramic Crucible

Brand: YUNXING
Product origin: China Jinzhou
Delivery time: 5-30 Days
Supply capacity: 3,000-5,000/month(Looking for distributors)

1. Aluminum Oxide Ceramic Crucibles are made of high-purity aluminum oxide, with an aluminum oxide content greater than 99% 2. Aluminum Oxide Ceramic Crucibles are resistant to chemical corrosion 3. Aluminum Oxide Ceramic Crucibles are resistant to high temperatures and can be used normally at 1600 ℃ and short-term at 1800 ℃ 4. Aluminum Oxide Ceramic Crucibles are resistant to sudden cold and heat, and are not easy to explode 5. Aluminum Oxide Ceramic Crucibles are formed by slip casting molding with high density

Email Annex

Aluminum Oxide Ceramic Crucible

My factory looking for distributors.

Advantages of Aluminum Oxide Ceramic Crucible

1. Aluminum Oxide Ceramic Crucibles are made of high-purity aluminum oxide, with an aluminum oxide content greater than 99%

2. Aluminum Oxide Ceramic Crucibles are resistant to chemical corrosion

3. Aluminum Oxide Ceramic Crucibles are resistant to high temperatures and can be used normally at 1600 ℃ and short-term at 1800 ℃

4. Aluminum Oxide Ceramic Crucibles are resistant to sudden cold and heat, and are not easy to explode

5. Aluminum Oxide Ceramic Crucibles are formed by slip casting molding with high density

Applications of Aluminum Oxide Ceramic Crucible

Aluminum oxide ceramic crucible is suitable for the analysis of various laboratory metal and non-metal samples and for melting materials.

Aluminum oxide ceramic crucibles can be used to burn pigments, colorants, frits, pigments, luminescent materials, etc. in shuttle kilns and push plate kilns.

Aluminum oxide ceramic crucibles are used for small experimental kilns, experimental electric furnaces, formula adjustment, and other purposes.

Aluminum oxide ceramic crucibles are used for melting metals, precious metals, and optical glasses.

Aluminum oxide ceramic crucibles are used for the analysis and firing of rare earth and other mineral raw materials, as well as the firing of high-temperature products such as ceramic powders.

Aluminum Oxide

The difference between aluminum oxide ceramic crucibles and evaporating vessels

Many people are not familiar with the difference between Aluminum oxide ceramic crucibles and evaporating vessels. Although there are many similarities between the two in use, there are still significant differences in actual use.

1. Different uses

Aluminum oxide ceramic crucibles can heat non aqueous substances, such as melting non corrosive salts, igniting precipitates, carbonizing or ashing certain complex specimens, etc; Evaporating dishes are generally used to evaporate solutions.

2. Different materials

The material of aluminum oxide ceramic crucibles must be resistant to high temperatures, and the upper temperature limit for ceramic crucibles is about 800 degrees Celsius; Aluminum oxide ceramic crucibles can be used at high temperatures above 1000 degrees Celsius, while evaporating vessels are usually made of ordinary glass or ceramics, and should be used at temperatures below 400 degrees Celsius.

3. Different heating methods

The aluminum oxide ceramic crucible can be directly heated or placed in a high-temperature heating furnace for heating; Ceramic evaporating dishes can also be heated directly with an open flame, while glass evaporating dishes usually need to be padded with asbestos mesh to be heated.

4. Due to the fact that crucibles are commonly used instruments in thermogravimetric analysis and have very precise quality requirements, it is generally necessary to use waste crucible pliers when using crucibles; The evaporating dish is usually taken by hand, and a glass rod or spoon can be used to transfer reagents.

5. The main purpose of aluminum oxide ceramic crucibles is to burn and precipitate, which can be used for high-temperature treatment of samples, such as ashing, charcoal burning, etc. The aluminum oxide ceramic crucible can withstand high temperatures of 1500 degrees Celsius. Ceramic evaporating dishes are mainly used for evaporating and concentrating liquids. When not subjected to quantitative analysis, they can also be used for drying solids, ashing filter paper, and high-temperature calcination (below 500 degrees Celsius).

Size,Performance index

Alumina crucible boats/Alumina ceramic trays
	Item NO.	Length (mm)	Width (mm)	Height (mm)	Volume (ml)	Item NO.	Length (mm)	Width (mm)	Height (mm)	Volume (ml)
1	175#	30	20	15	5	076B	50	10	10	2
2	113A	62	32/22	16	18	161#	65	65	65	180
3	154#	80	50	7	20	171#	80	55	15	47
4	076A#	100	10	10	5	075#	100	20	20	28
5	155#	100	30	30	75	114#	100	40	18	55
6	226#	105	22	14	22	227#	184	123	62	1120
7	138#	300	36	18	132	113B#	300	45/30	20	20
8	254#	200	100	50	770	273#	84	13/11	8	7
9	274#	45	13/11	9	5	297#	48	50/10		19
10	303#	100	50	30	100	341#	150	35	25	86
11	338#	100	20	20	28	344#	100	35	20	46
12	355#	60	30	20	22	359#	130	130	60	793
13	360#	145	145	12	128	372#	60/10	30	20	20
14	373#	60/10	50	30	63	382#	175	90	26	254
15	396#	100	100	17.5	100	414#	250	100	70	1400
16	415#	250	56	50	497	440#	250	46/15	15	65
17	444#	50	20	20	13	477#	70	36	17	27
18	493#	44	33	17	16	507#	52	31	6	5
19	514#	120	60	17	66	515#	120	60	14	50
20	523#	105/80	18/14	12	15	526#	200	20	15	30
21	539#	150	150	70	1275	429#	69	22	11	12
22	575#	200	100	40	600	591#	313	45	30	335
23	606#	76.2	12.7	12.7	7.5	614#	120	83	53	385
24	630#	160	160	50	1015	636#	50	40	20	27
25	643#	170	170	27	370	673#	75	15	10	6
26	678#	190	190	80	2430	689#	101.6	38.1	21.08	58
27	695#	200	200	50	1620	707#	114.3	76.2	9.6	470
28	644#	120	80	22	160	662#	64	64	60	210
29	718#	90	17	11.5	9	724#	120	30	20	48
30	728#	100	35	15	35	747#	50	12	10	3
31	776#	64	38	20	34	791#	48	30	24	16
32	796#	88.9	88.9	44.45	260	803#	130	80	15	97
33	799#	188	140	42	850	822#	110	70	35	180
34	825#	50	29	28	30	829#	300	65	30	460
35	837#	300	60	30	410	838#	108	45	19	68
36	849#	150	15	10	12	871#	76	76	21	46
37	879#	83	52	6.5	17	886#	130	90	140	1300
38	889#	100	100	27	180	890#	120	60	25	135
39	906#	206.38	152.4	133.35	3560	907#	165.1	111.76	104.78	1560
40	910#	50.8	50.8	6	8	916#	150	65	19	140
41	918#	250	200	100	4300	919#	200	150	100	2500
42	920#	170	170	100	2400	921#	190	190	100	3000
43	959#	300	220	70	3950	966#	160	47	23.5	115
44	978#	65	30	17	21	989#	50	12	9	2.5
45	990#	70	14	10	5	992#	62	22	16	15
46	A20#	83	12.7/11.7	4.5	5	805#	13	13	8	0.6
47	A39#	18	100	10	9	A51#	190	190	50	1460
48	A52#	65	65	30	90	A59#	100	45	19	60
49	A92#	95	48	74	215	A93#	107	60	69	330
50	A94#	150	80	55	450	A95#	250	200	120	5240
51	B18#	220	45	50	330	B19#	54	38	20	25
52	B23#	40	30	6	5	B34#	15	8	100	5.5
53	B71#	40	100	20		B72#	58	145	29
54	B90#	125	125	85		B96#	105	22	14.5
55	B99#	70	70	30		C07#	125	60	20
56	C09#	137	27	21		C34#	250	250	50
57	C75#	140	140	60		C81#	100	14	12
58	C84#	150	150	95		C88#	75	50	11
59	D12#	50	12	10		D13#	75	15	10
60	D14#	90	17	11.5		801#	55/45	13	9/2
61	D37#	205	100	300		D54#	120	30	15

Alumina ceramic performance index (Notice of Correct in Leakeage Rate）

NO.	Property	Unit	Alumina
1	Al₂O₃	%	>99.3
2	SiO₂	%	—
3	Density	g/cm³	3.88
4	Water absorption	%	0.01
5	Compressive strength	MPa	2300
6	20℃ leakage rates	Torr・L/sec	>10^-11=1.33322×10^-¹²Pa・m³/sec
7	Twisting in high temperature	mm	0.2 allowed in 1600℃
8	Bonding in high temperature		not bonded in 1600℃
9	20—1000℃ coefficient of thermal expansion	mm.10^-6／℃.m	8.2
10	Thermal conductivity	W/m.k	25
11	Electric insulation strength	KV/mm	20
12	20℃direct current insulation resistance	Ohm/cm	10¹⁴
13	High-temperature insulation resistance	1000℃ MΩ	≥0.08
13	High-temperature insulation resistance	1300℃ MΩ	≥0.02
14	Thermal shock resistance		4 times not cracked in 1550℃
15	Maximum working temperature	℃	1800
16	Hardness	Mohs	9
17	Flexural strength	Mpa	350

Our factory

Jinzhou Yunxing Industrial Ceramics Co., Ltd. was established in 2000, mainly producing various types of tubular ceramic products and various industrial parts with alumina content above 99.3%. The factory covers an area of 4000 square meters.

The company's main products are: alumina ceramic tubes, alumina ceramic crucibles, alumina ceramic rods, alumina ceramic boats, alumina ceramic plates, alumina ceramic parts, etc.

The company currently has 3 1800 ° C high-temperature furnaces and 2 1400 ° C low-temperature kilns independently designed and manufactured. The molding process is mainly based on grouting molding, and has other molding process equipment such as extrusion and hot die casting.

The company has 105 employees, including one senior ceramic engineer, three engineers, six overseas sales staff, and four professional after-sales staff.

FAQ

Q1. What information should we supply to get a quote?

A1. Please offer the specification of aluminum oxide ceramic crucible, such as shape, dimension, quantity, application etc.

Q2. What is aluminum oxide ceramic crucible used for?

A2. Used as a material for industrial furnaces due to its ability to maintain its hardness at high temperatures. Used as a protector for high-temperature thermal couples. Used as a material for the chemical industry due to its high corrosion resistance.

Q3. Is aluminum oxide ceramic crucible the same as aluminum oxide?

A3. Alumina ceramic, or aluminum oxide (Al2O3), is an industrial ceramic that has high hardness, is long wearing, and can only be formed by diamond grinding.

Q4. What is the temperature of aluminum oxide ceramic crucible?

A4. The maximum working temperature of aluminum oxide ceramic crucibles can be up to 1800℃. Provides high-quality Al2O3 crucibles with good electrical insulation, excellent corrosion resistance, and excellent thermal shock properties.

Crucible